Higlue PC 9313 7227 putty epoxi Resin Devcom wear protection coating 2 part epoxy putty
2024-10-11 16:07:35
admin
15
* Protects against fine particle abrasion
* Trowelable - easy to mix and apply
* Can be used on overhead or vertical surfaces
* Prolongs equipment life
* Trowelable - easy to mix and apply
* Can be used on overhead or vertical surfaces
* Prolongs equipment life
Ceramic Repair Putty
* Renews worn surfaces fast and reduces
* Downtime to put equipment back in service
* Quickly Easy to mix and use
* Non-sag paste allows application
* Versatility for overhead& vertical surfaces
* Non-shrinking
* Extends wear life
* Resists sliding abrasive wear
* Eliminates costly wear part
* Inventory Can be re-applied to
* itself Contains ceramic beads 1-1.5mm
Technical information
Application
1. Cyclone and separator bodies
2. Dust collectors and exhausters
3. Pump liners and impellers
4. Fan blades and housings
5. Chutes and hoppers
6. Elbows and transition points
2. Dust collectors and exhausters
3. Pump liners and impellers
4. Fan blades and housings
5. Chutes and hoppers
6. Elbows and transition points
How To Use
1. Cleaning:Remove dirt,oil, grease,loose flanky rust etc.,with a suitable high pressure water cleaning system .
2. Blasting:Blast all surfaces to be coated,with a sharp edged angular grit,such as aluminum oxide,to a depth of profile of
approximately 75 microns and a degree of cleaniness of very thorough Blast Claeaning/Near Whitef.
3. Cleaning:After blasting metal surfaces should be cleaned with a waterless or solvent,and allow the surface to dry before
application of the product coat the surface before any oxidation or contamination takes place.
4.Protection From Flash Rusting:To avoid flash rust,repairs should be made as soon as possible or within a mixmum 2 hours of
blasting.
5. Mixing The Material:Measure 2 parts resin to 1 part hardener by volume or weight if doing a partial kit.Otherwise,mixing a full
kit is pre-measured at the correct ratio.For a full kit mix ,a spiral mixing blade attached to a high torque electric or pneumatic
drill can be used.For a partial kit transfer measured quantities onto a clean and dry mixing surface to mix together witha trowel
until uniform in color.If resin and hardener temperatures are 15ºC or below,preheat resin only,to about 30ºC but not to exceed
40ºC.
6. Application:Apply fully mixed material to the prepared surface.Initially apply the material in a very thin layer to "wet" out
the surface and ensure full epoxy contact with the roughened surface. Build up to desired thickness(minimum 6 mm),avoiding air
entrapment.At 25ºC,the working time is 15 minutes and functional cure time is 4 hours Working and cure time depend on temperature
and mass the higher the temperature and the larger the mass,the faster the cure.
2. Blasting:Blast all surfaces to be coated,with a sharp edged angular grit,such as aluminum oxide,to a depth of profile of
approximately 75 microns and a degree of cleaniness of very thorough Blast Claeaning/Near Whitef.
3. Cleaning:After blasting metal surfaces should be cleaned with a waterless or solvent,and allow the surface to dry before
application of the product coat the surface before any oxidation or contamination takes place.
4.Protection From Flash Rusting:To avoid flash rust,repairs should be made as soon as possible or within a mixmum 2 hours of
blasting.
5. Mixing The Material:Measure 2 parts resin to 1 part hardener by volume or weight if doing a partial kit.Otherwise,mixing a full
kit is pre-measured at the correct ratio.For a full kit mix ,a spiral mixing blade attached to a high torque electric or pneumatic
drill can be used.For a partial kit transfer measured quantities onto a clean and dry mixing surface to mix together witha trowel
until uniform in color.If resin and hardener temperatures are 15ºC or below,preheat resin only,to about 30ºC but not to exceed
40ºC.
6. Application:Apply fully mixed material to the prepared surface.Initially apply the material in a very thin layer to "wet" out
the surface and ensure full epoxy contact with the roughened surface. Build up to desired thickness(minimum 6 mm),avoiding air
entrapment.At 25ºC,the working time is 15 minutes and functional cure time is 4 hours Working and cure time depend on temperature
and mass the higher the temperature and the larger the mass,the faster the cure.
Company Profile
Jiangxi Gooz Adhesive Co., Ltd
Bldg, B3, Gongye Road, Lutang Village, Yining Town, Xiushui County, Jiujiang City,Jiangxi Province,China.www.hi-glue.com Email:LISA001@JXGOOZ.COM
BUSINESS HOURS
Monday-weekend:Spring& Summer: 9am to 6pm Autumn& Winter: 9am to 5:30pm